废旧橡胶的回收利用.doc

废旧橡胶的回收利用——胶粉的物理化学法制备摘要胶粉是废旧橡胶经过机械粉碎制得的颗粒状粉体, 具有致密的交联网络结构, 但被人们长期使用的废旧橡胶表面已失去活性, 因此, 胶粉在应用到其他材料时, 与基质材料的相容性很差, 导致复合材料的性能不理想。然而, 对胶粉进行表面改性, 是解决这一瓶颈的关键所在。本文针对胶粉的再利用难题, 开展了一系列的胶粉表面改性的研究工作: 采用微波脱硫改性方法和机械力化学改性方法对胶粉改性, 进而将改性胶粉应用到橡胶材料中制备了胶粉/天然橡胶硫化胶, 并探讨了两种方法的改性效果。最后, 为进一步扩大胶粉的应用领域, 结合机械力化学改性方法制备了改性胶粉/ 丁***橡胶发泡材料, 并研究了其相关性能。本文主要采用纯度为 90% 以上的胶粉为原料, 研究了该胶粉与橡胶基质中的应用情况。关键词: 精细胶粉; 粒度; 物理化学法; 延伸率; 抗拉强度; Recycling of Waste Rubber —— Ultrasonic D esulphurization and R e-vulcanized Abstract Waste rubber powder (WRP) is granular powder which is made from waste rubber grinded by rubber powder (WRP) with dense cross-work structure has lost its surface activity, because waste vulcanized rubber is used by people for a long time. Therefore, when waste rubber powder (WRP) is applied for other materials, patibility beween WRP and the matrix material is very poor, so that the properties posites is not ideal. However, surface modification of WRP is the key to solve ... . Keywords : fine-grade rubber power;grade;physicochemistry method;elongation coefficient;tensile strength; 目录摘要………………………………………………………………………………… 1 ABSTRACT ……………………………………………………………………… 2 前言………………………………………………………………………………… 4 第一章概述……………………………………………………………………… 5 ………………………………………………5 …………………………………………………5 第二章废旧橡胶再生方法…………………………………………………… 9 传统的再生方法……………………………………………………………9 现代的再生方法…………………………………………………………… 9 第三章废旧橡胶的物理化学法制备胶粉………………………………… 13 废旧橡胶的传统制备胶粉法……………………………………………… 13 常温粉碎法…………………………………………………………… 13 低温粉碎法…………………………………………………………… 15 湿法或溶液粉碎法…………………………………………………… 17 物理化学法制备精细胶粉………………………………………………… 18 物理化学法处理工艺………………………………………………… 18 试验结果分析………………………………………………………………… 19 物理化学法与普通粉碎法的比较…………………………………… 19 胶粉∕介质体积比对胶粉粒度的影响……………………………… 20 胶粉力学性能的比较………………………………………………… 20 第四章结论……………………………………………………………………… 24 物理化学法的优点………………………………………………………… 24 废旧橡胶的未来发展趋势………………………………………………… 24 参考文献………………………………………………………………………… 26 致谢………………………………………………………………………………