基于正交试验法的管桩离心工艺优化.doc

基于正交试验法的管桩离心工艺优化
何建明
(浙江广天构件股份有限公司,浙江宁波 315021)
Based on orthogonal testing method steel pipe driven in as piling gentrifugalism craft optimization
HeJianMing
(Zhejiang ponent Part limited pany, Zhejiang Ningbo 315021)
[摘要]本文通过正交试验法探索管桩最佳离心工艺,找出了离心工序影响混凝土密实度的主要因素,从而优化了离心工艺参数,保证了管桩质量,提高劳动生产率,降低生产成本,同时为优化管桩离心工艺提供一种方法和经验。
[关键词]管桩离心工艺正交试验法优化
Abstract:Through the orthogonal testing method exploration steel pipe driven in as piling best gentrifugalism craft practice, has discovered the centrifugal working procedure influence pactness primary factor, the optimized gentrifugalism craft parameter, guaranteed the steel pipe driven in as piling quality, enhances the labor productivity, reduces the production cost, simultaneously provides one method and the experience for the optimized steel pipe driven in as piling gentrifugalism craft.
Key word:Steel pipe driven in as piling gentrifugalism craft;Orthogonal testing method;Optimization

离心成形对于预应力混凝土管桩制造是一个十分重要的工序,是确保管桩混凝土达到良好密实度的关键工序。国内外对离心工艺中的离心加速度、离心时间与不同坍落度混凝土料离心后混凝土的强度、密度、剩余水灰比等之间的关系的研究已相当成熟,为各管桩生产厂家离心工艺的编制提供了理论基础,但各生产厂家的混凝土配比、减水剂品种与用量、掺与不掺磨细矿物质、离心机与模具工作状态不同,很难有一个规定的离心工艺,而要获得最佳管桩离心工艺,关键是在离心工艺相关理论指导下根据生产实际条件通过试验确定。
宁波地区管桩应用量较大,生产厂家也较多。从对部分生产厂家的考察中发现管桩的离心工艺中普遍存在下列现象:高速离心速度较高,离心时间较长,管桩离心后内壁比较光滑,外观美观,但当管桩在锤击过程中被击碎时,往往发现混凝土分层较明显。我们认为其主要原因是离心工艺不佳,没有经过生产实践的系统试验。因影响离心工艺的因素很多,要找出最佳的离心工艺需进行大量的试验,大多厂家没有时间和精力,只能凭经验。本文通过正交试验法,用尽可能少的