多极镁电解槽热槽现象的探讨
周云英,石玉英
(攀枝花钢企欣宇化工钛业分公司,四川攀枝花 617000)
摘要:多极镁电解过程中电解产出的金属镁与***气发生二次反应使槽温升高、电流效率降低、单槽产量减少,即所谓的热槽现象。对此热槽现象进行深入分析和探讨,并提出相应的处理措施。
关键词:镁电解;电解槽;热槽现象;措施
中图分类号:TF822 文献标识码:A 文章编号:1007-7545(2012)12-0000-00
Study on Occurrence of Hot Cells in Multipole Magnesium Electrolyzer
ZHOU Yun-ying, SHI Yu-ying
(Titanium Industry pany, Panzhihua Gangqi Xinyu Chemical Industry Co., Ltd, Panzhihua 617000, Sichuan, China)
Abstract: Hot cells frequently occurred in electrolytic process of magnesium. The second reaction between magnesium metal and chlorine abnormally led to rise of electrolyzer temperature, decrease of current efficiency and production reduction in single cell. This phenomenon in multipole magnesium electrolyzer is analyzed with in-depth discussion and the measures are put forward.
Key words: magnesium electrolysis; electrolytic cell; occurrence of hot cell; measurement
多极镁电解槽在正常运行情况下,电解槽温度基本上都处于655~660 ℃的低恒温状态,当槽温偏高时启动风机冷却降温,温度偏低时则启动交流加热系统升温,但在生产过程中,槽温往往呈上升趋势,即产生热槽现象,多极镁电解槽正常热槽可通过间歇式启动风机快速降温,但当热槽严重时启动风机是无法使槽温恢复正常的,甚至会持续飙升使槽温完全失控,此时电流效率由85%降低至30%以下, t/ t/d以下,吨镁综合电单耗则由12 800 kWh上升至23 800 kWh。
为提高多极镁电解槽电流效率,就必须尽量减少热槽现象的发生,同时对产生的热槽问题及时分析和处理,在最短时间内使槽温恢复正常,降低热槽损失。本文仅针对本公司在多极镁电解槽生产过程中出现的热槽现象及解决处理措施进行分析探讨。
1 热槽现象产生的原因

***化镁熔体中氧化镁杂质的影响
多极镁电解槽的主要原料是还蒸工序产生的副产品——熔体***化镁,由于***化镁具有极强的挥发性和吸湿性,在***化镁熔体转运过程中要求密闭不与空气接触。但在实际操作中往往会因各种原因造成***化镁不能与空气完全隔离,从而生成氧化镁杂质。其反应方程式为:
MgCl2+H2O=MgO+2HCl↑
2Mg(l)+O2=2MgO
产生的氧化镁杂质随***化镁熔体带入电解槽后,容易被吸附在阴极表面使阴极钝化,阴极发生钝化后,镁不能在阴极汇集长大,而分散在电解质中[1],分散在电解质中的液镁与电解质中的***气发生二次反应引起热槽,加入电解槽***化镁熔体中的氧化镁杂质含量越高,越容易使阴极钝化,液镁与***气越容易发生二次反应,热槽也越严重。表1为110 kA电解时***化镁中氧化镁杂质含量对3#槽槽温的影响。
表1氧化镁含量对3#槽槽温的影响
Table 1 Effect of content of magnesium oxide on temperature of electrolytic cell
MgO/%
电解质中MgO含量/%
升温速度/(℃·min-1)
电流效率/%

43
-


40
-


30
+


00
+


00
+


30