叶腊石制品的再研制和探索
单志强王国华张泽
(重庆钢铁集团矿业有限公司重庆耐火材料厂)
 
摘要由于生产粘土砖用原料的价格不断上涨,并且现用原料资源有限,导致生产成本的不断上升,在此形势下研究利用叶腊石较高的荷重软化温度、高温状态下的微膨胀性能、烧成温度低及广泛的叶腊石资源生产含叶腊石及叶腊石制品。而且叶蜡石价格可以接受,资源较近。故本次试验以引入叶腊石为主要目的进行配料,烧成温度稳定并能满足生产工艺和产品使用的要求。
关键词叶蜡石成本粘土砖
Abstract As the production of clay brick with the rising prices of raw materials and raw materials resources are limited, leading to rising production costs, in this situation, study, pyrophyllite high refractoriness under load, high temperature under the micro-expansion properties, sintering temperature and extensive resources for low-production with pyrophyllite and pyrophyllite pyrophyllite the price is acceptable pyrophyllite, resources closer. Therefore,the introduction of this test in order to carry out the primary purpose of pyrophyllite ingredients,firing temperature stable and can meet the production process and product requirements.
Keywords pyropyllite cost clay brick
一、概述
一般蜡石含Al2O315%~30%,SiO270%~85%,其他杂质成分很少,是良好的半硅质耐火原料。很多国家都试制过蜡石质耐火材料,很早以前美国就将大块蜡石凿成砖块,砌筑烟囱和炉底,俗称耐火石或炉石;日本以蜡石为原料制造耐火材料,已有百年历史,至今仍然大量生产蜡石质耐火材料;苏联于1936年就试制过蜡石质耐火材料,现仍然进行蜡石砖的研究;巴西、澳大利亚、印度等国家利用本国蜡石生产盛钢桶衬砖、袖砖、下注流钢砖;在马鞍山钢铁公司、鞍山钢铁公司、宝钢等小型、中型、大型盛刚桶上试用,中小型盛刚桶的使用寿命较粘土砖提高近一倍,大型盛刚桶使用效果也明显较粘土砖好。
叶蜡石是粘土矿物的一种,属结晶结构为2∶1型的层状含水铝硅酸盐矿物。化学结构式为Al2[Si4O10](OH)2,%, %,%,。叶蜡石是低温热液蚀变形成的粘土矿物,属单斜晶系,晶体结构高度无序。叶蜡石质地细腻,硬度低(1-2°),-