超高温材料硼化锆粉体的制备毕业论文.docx

超高温材料硼化锆粉体的制备毕业论文.docx毕业论文
超高温材料硼化错粉体的制备
学 院：—
专 业：
学生姓名：
学 号：
指导教师：
2012年06月
中文摘要
中文摘要
论文采用在真空中利用碳还原法进行硼化错粉体的制备，该方法是以氧化 错、活性炭、碳化硼和氧化硼为主要原料，研制出纯度较高，颗粒较小且制作工 艺简单、成本较低的硼化错粉体。本文主要研究在碳热还原反应中，碳含量、烧 成温度和保温时间对反应产物的影响。通过对反应产物进行XRD、SEM等测试 分析，找到一条制取高质量硼化错粉体的反应路线：（1）碳含量要过量；（2）烧 成温度为1650°。
关键词：碳热还原法硼化错碳含量反应温度保温时间
Abstract
Abstract
The ZrB2 powers are prepared in vacuum by carbothermal reduction method with ZrO2 powers 32O3 powers, B4C powers ,and activated carbon as the main raw material. Lower cost of ZrB? powers have been developed which have high purity, smaller particles and simple production technology. This paper mainly studies effect of the content of carbon content, sintering temperature and holding time on the influence of reaction products in carbothermal reduction method. Through testing and analyzing the SEM, XRD of the ZrB? powers, the results show that high quality ZrB2 powders can be synthesized with the optimum processing parameters as follows: (i) Activated carbon should be excessive; (ii) the condition of carbothermal reduction heat treatment is at 1650°C for .
Key words: carbothermal reduction method, ZrB? powers, carbon content, reaction temperature, the time of heat
目录
中文摘要 1
ABSTRACT （英文摘要） I
第一章：引言 1
： 1
2
2
3
4
5
6
7
、内容和目标 7
第二章试验方法 9
： 9
： 9
： 9
： 10
： 11
： 12
： 12
： 12
： 13
第三章结果与讨论 14
XRD衍射图谱分析（物相分析） 14
14
16
18
ZRB2粉体显微结构分析 20
第四章结论 23
参考文献 24
致谢 错误！未定义书签。
第一章：引言
：
在科学技术日新月异的今天，世界新材料的迅猛发展对先进材料的性能提出 越来越高要求，而制备高性能材料必须以高纯、超细的无机化合物为原料。因此, 生产高性能、低成本的原料市场潜力巨大。先进陶瓷材料的优良性能是通过其 特殊的化学组成和微观结构来实现，而这又需要陶瓷加工过程各个工艺步骤的精 细控制。现代陶瓷的制备工艺过程主要有粉体制备、成型、烧结三个主要环节组 成。其中，粉体制备是基础，是原料的准备阶段，若粉体质量不高，不但烧结条 件难