SDS和LAS改性构树皮对铀的吸附（毕业设计论文doc）.doc

SDS和LAS改性构树皮对铀的吸附

摘要:以构树皮为原料,经LAS或SDS改性,得到一种高效吸附剂。本实验初步研究了改性构树皮吸附废水中铀的影响因素,并探讨了其对铀的吸附性能。研究结果表明,构树皮最适宜的改性条件为:构树皮粒径1mm,SDS或LAS的浓度10g/L,改性温度25℃,120rpm,改性时间48h。构树皮对铀离子的最佳吸附条件为:,温度24℃,最佳吸附时间为60min。该改性构树皮的吸附符合Freundlich型吸附等温曲线。本试验证明SDS改性最好,其余依次为LAS改性和未改性构树皮。
关键词:构树皮; 吸附; SDS; LAS; 铀;
Adsorption of Uranium by
SDS and LAS modified Papermulberry bark
Abstract:Using the papermulberry bark as raw material, modified by LAS or SDS, one kind of adsorbents can be got. The affecting factors of adsorption on Uranium in uranium solution were studied by the modified papermulberry bark. The results showed that the most appropriate condition of modifying the papermulberry bark is that bark size is 1mm, concentration of SDS or LAS is 10g/L, the temperature is 25℃, the speed of shaker is 120 rpm and the contact time is 48h. The most appropriate adsorption conditions are that pH value is , temperature is 24℃ and the contact time is 60min. The adsorption of the modified bark corresponded with Freundlich. This experiment proved that the papermulberry bark modified by SDS had the best effect, and then the LAS, last the unmodified Papermulberry bark.
Key words: Papermulberry Bark, Adsorption, LAS, SDS, Uranium
目录
第1章绪论 1
概述 1
重金属污染 1
重金属定义 1
重金属污染的主要来源 2
重金属污染的现状与危害 3
重金属对水体污染的现状与危害 3
4
重金属污染的处理方法分类 5
化学法 5
物理法 6
吸附法处理重金属的研究进展 7
吸附的材料种类 7
吸附作用的机理 8
影响离子吸附性能的因素 9
本课题的研究内容、目的与意义 10
研究内容 10
研究的目的与意义 10
第2章材料与方法 11
试验材料与仪器 11
材料 11
化学试剂 11
主要仪器 11
试验方法与步骤 11
药品配制 11
材料预处理 12
试验方法 12
第3章结果与分析 15
构树皮改性前后红外光谱分析 15
铀浓度标准曲线 16
***乙酸-***乙酸钠缓冲液pH值测定如下表 17
不同影响因素对构树皮吸附铀的影响 18
不同pH值对构树皮吸附铀离子的影响 18
不同温度对构树皮吸附铀的影响 19
铀离子初始浓度对构树皮吸附铀离子的影响 20
同一浓度下的最佳吸附剂量 21
三种构树皮吸附铀离子的最佳吸附时间 22
构树皮吸附铀离子的动力学方程 24
构树皮吸附铀离子的等温曲线 24
第4章讨论 27
改性剂对构树皮的影响 27
pH值对吸附铀的影响 27