,黄晓因(;,云南昆明 650201) 摘要:在液氮温度(一196~C),处理时间分别为72h、120h,并进行了力学性能试验和金相组织分析。试验结果表明,深冷处理显著提高了合金的强度和硬度,经适当时间的深冷处理,强度、硬度及伸长率三者能同时提高。初步的研究认为,深冷处理改善铝合金性能的机理主要是处理后合金中产生大量相互缠绕的位错和析出弥散强化相。关键词:;深冷处理;力学性能;显微组织中图分类号:; 文献标识码:A 文章编号:0254~051(2005)08-0055-03 Effect0fCryogenicTreatmentontheMicrostructureandMechanical ,! (;puterScienceDepartment, YunnanAgriculturalUniversity,KunmingYunnan650201,China) Abstract:SomecryogenictreatmentexperimentswerecarriedoutonA1一Sialloyatliquidnitrogentemperature (一196~C)for72hoursand120hoursrespectively,andthemechanicalpropertiesweretestedandthemicrostructures ~resultsshowthatthestrengthandhardnessoftheA1一Sialloycanbeen— hancedremarkablythroughcryogenictreatment,moreover,allofthestrength,hardnessandductilitycanbeincreasedat thesametimeifcryogenic— thepropertiesofA1一Sialloysthroughcryogenictreatmentismainlyduetoproducingalotoftangleddislocationsand somedispersionprecipitates. Keywords:A1一Sialloys;cryogenictreatment;mechanicalproperties;microstructure 深冷处理能改善金属材料的性能,增强耐磨性,延金6的深冷处理中同样发生了类似的马氏体型相变。长工件的使用寿命。在高速钢l’及模具钢3l4j的研然而在铝合金的深冷处理中没有相变发生,其深冷处究方面已取得重要成果。深冷处理的一个最突出的优理的改性机理有别于钢铁材料。本文作者主要研究深