材料成型论文.doc

材料成型论文
焊接熔渣的作用
杨晓欢质监学院11机械 2011452027
[摘要]焊接冶金过程是包括金属、熔渣、气体三者在内的一个体系,熔渣是其中一个极为重要的因素。焊接过程中,焊(钎)剂和非金属夹杂互相溶解,经化学变化形成覆盖于焊(钎)缝表面的非金属物质,形成焊接熔渣。其在焊接冶金过程中有利有弊,为使焊接熔渣起到人们预期的良好作用,关键在于通过调整和控制熔渣的化学成分使其具有合适的物理化学性质。
[关键词]焊接熔渣焊缝质量物理化学性质脱氧脱硫 The effect of welding slag
[Summary]Welding metallurgical process is including metal, slag and gas, a system,and slag is one of the very important factors. During the welding process, welding (bit) agent and non-metallic inclusion dissolve each other, the chemical changes in formation on the surface of the weld seam (bit) are covered with non-metal material, welding slag formation. Its deeply in the process of welding metallurgy, to make the welding slag have expectations of good effect, is the key to adjust and control the position of slag has the appropriate physical and chemical properties.
[Keywords]Welding slag Weld quality The chemical and physical properties Remove oxygen Remove sulfur.
引言
在电弧焊过程中,由于电弧高温的作用,使基本金属部分熔化,形成一个凹坑,称为熔池。焊接时,熔池周围充满着大量的气体和熔渣,这些气体、熔渣和液态金属之间不断地进行着复杂的冶金反应,这些反应在很大程度上决定着焊缝金属的质量。本文主要研究熔渣对焊缝的成分和性能的影响。
一、熔渣的组成和作用
(一)熔渣的组成
熔渣是由金属和非金属的氧化物组成的。这些氧化物按照它们的化学性质,可分为三类:
1、酸性氧化物,如二氧化硅(SiO2)、二氧化钛(TiO2)、五氧化二磷(P2O5)、三氧化二硼(B2O3)等。
2、碱性氧化物,如氧化钾(K2O)、氧化钠(Na2O)、氧化钙(CaO)、氧化镁(MgO)、
1
氧化锰(MnO)、氧化亚铁(FeO)等。
3、中性氧化物,氧化铝(Al2O3)、氧化铁(Fe2O3)、氧化铬(Cr2O3)、氧化钒(V2O3)等。它们又称为***氧化物,即在强酸性熔渣中常常呈弱碱性,而在强碱性熔渣中,常常成弱酸性。
上述三类氧化物,在熔渣中主要以复杂的硅酸盐