金属超细粉体制备.doc

金属超细粉体制备
存档日期: 存档编号
北京化工大学
研究生课程
课程名称: 超细粉体制备
课程代号: ChE583
任课教师: 毋伟
完成日期: 2011 年 12 月 29 日
专业: 化学工程与技术
学号: 2011200170
姓名: 程治化
成绩:
超细粉体制备课程论文
金属超细粉体的制备方法
程治化
(北京化工大学化学工程学院,北京市朝阳区,100029)
摘要:本文介绍了一些制备金属超细粉体的方法,主要是制备用于水反应金属燃料的金属粒子所采用的电爆炸法和电弧等离子法,制备高纯度、粒度均匀的超细金属粉末所用的电解法以及以传统电解法为基础的超声波法,超声波法克服了传统电解法的一些缺点,制得的粉末颗粒较细且不易团聚。
关键词:金属超细粉体;制备;电爆炸法;电弧等离子法;电解法;超声波
Abstract: This article introduces some methods of preparation of ultrafine metal powders. It mainly includes electrical explosion method, Arc plasma method, electrolysis method and ultrasonic method based on the traditional electrolysis method. The electrical explosion method and Arc plasma method are used to prepare superfine powder of metal used as metal fuel for water reaction. The superfine powder of metal prepared by electrolysis method has some good properties. It is epigranular and has high purity. The ultrasonic method has e some ings of traditional electrolysis method. The obtained powder has thin particle size and is not easy to get gather.
Key Words: ultrafine metal powders; preparation; electrical explosion method; Arc
plasma method; electrolysis method; ultrasonic
前言
超细粉体的定义尚不统一,一般分为微米级粉体(1μm < x < 100μm)、亚微米级粉体( < x < 1μm)、纳米粉体( < x < )。它属于微观粒子和宏观物体之间的过渡区域,由于超细颗粒具有比表面积大、表面活性高等特点,使其具有一系列特殊的物理、化学性能,因而被广泛应用于宇航、
[1]国防、化工、冶金、电子、生物工程和核工业等方面。当今超细粉体材料产业
化项目中就其应用的成熟性和规模仍以亚微米粉体居多,纳米粉体次之。但纳米粉体有很大的潜在市场需求。产业化超细粉体主要为超细金属粉体,如:Al,Ni,Zn,Fe,Cu,Ag及其些合金超细粉体,其中Ni、Zn为亚微细粉体,Al,Fe,Cu,Ag 为纳米粉体;超细陶瓷粉体,如:ZrO2、Al2O3、Bi2O3、Fe2O3、SiO2、ZnO等超细粉体;超细铁氧体粉体。
对于超细粒子的制备已有许多方法,根据反应体系的不同可分为气相法、液
[2]相法和固相法。气相法一般是指用气体原料或将原料蒸发成气体,然后通过化
学反应或物理作用再生成超细颗粒的方法。这类方法中包括气相化学反应、激光
1
超细粉体制备课程论文
合成法、电爆炸法、惰性气体冷凝法和电弧等离子体法[3]。液相法是当前实验室和工业上广泛采用的合成高纯超细粉体的方法,可分为沉淀法、水解法、溶胶一凝胶法、微乳液法和溶剂蒸发法等。固相法目前主要采用的是机械法(也称粉碎法)。它采用研磨或气流、超声方法将块状物质粉碎、细化,从而得到不同粒径范围的超细颗粒。金属超细粉体的制备,主要有电爆炸法、电弧等离子法、电解法和超声波法等。对于用作水反应金属燃料的金属粒子,通常采用电爆炸法和电弧等离子法;而制备高纯度、粒度均匀、且表面包覆的超细金属粉末,采用电解法较好;有些需在高电流密度下电解相应的电解质水溶液制备的金属粉