掺杂氧化锌铝对可钢LowE玻璃的性能改善.pdf

掺杂氧化锌铝对可钢Low-E玻璃的性能改善 Improvement of theperformance fortemperable Low—E glass affected zincoxidelayer 岳志峰天津耀皮工程玻璃有限公司天津300409 摘要本文从两方面研究了掺杂氧化锌铝对可钢Low-E玻璃的性能改善。通过磁控溅射的方法制得了三种不同膜层结构的Low-E玻璃,比较了不同结构的Low-E镀膜玻璃的性能及可钢化性。较深入地阐述了掺杂氧化锌铝对可钢Low-E玻璃辐射率及耐磨性的影响机理。 Abstract This paper studied the improvement ofthe performance for temperable low-E glass that affected by aluminum-doped zinc oxide layer from two different structures of low-E glasses were prepared by the ron sputtering system,and the performance of each type ofglass paper studied the reliability ofthree different structures during heating mechanism of emissivity and resistance toabrasion oftemperable low-E glass affected by aluminum-doped zinc oxide layer was deeply explained. 关键词可钢Low-E氧化锌耐磨性 Key words temperable 10w-E zinc oxide resistance to abrasion 引言平板玻璃发展到今天,已经越来越多的作为镀膜深加工的原材料而并非最终产品。经过镀膜的玻璃具有很高的附加值,成为广泛应用于建筑、汽车、显示等工业领域的高级产品u1。随着国家《节能法》的颁布与实施,低辐射玻璃也得到越来越广泛的应用。近年来为了大规模推广和使用低辐射镀膜玻璃,可钢化低辐射玻璃得到了快速发展。可钢Low-E镀膜玻璃由镀膜生产厂家进行大规格玻璃尺寸的镀膜,这样有利于下游中型深加工企业进行钢化和中空,可节约运输成本,专业强化,分工合作,有利于提高镀膜生产厂家的效率和效益,是中国以后发展建筑节能产品的有效途径旧1。高透过率型可钢Low-E玻璃普遍存在性能不好,钢化后雾化以及耐磨性能不好的问题。通过磁控溅射形成的ZnO薄膜,是一种典型的纤锌矿结构,已有文献报道过在锡基Low-E中,结晶良好并且界面光滑的ZnO薄膜可以显著提高Ag在其界面上的结晶效果,进而降低Low-E玻璃的面电阻,提升其性能∞1。在以前的报道中,Park等人将铝离子(53pm)取代了Zn离子从而形成了铝掺杂的氧化锌晶体薄膜H’。铝掺杂的氧化锌可以减小氧化锌与Ag之间的界面应力,从而可以提高此种结构Low-E 的抗氧化性哺H利。而可钢Low-E的钢化过程是加热后膜层重新结晶的过程,所