2009年12月·第26卷·第6期 轧钢 STEEI。R()I。I。仆JG 9 加磷高强IF钢冷轧板罩式退火工艺研究左军1,常军1,张开华1,杨金成2,黄徐晶2 (,四JII 攀枝花 617000; ,四川I 攀枝花 617067) 摘要:在实验室条件下测定了P1F340加磷高强IF钢的再结晶温度,研究了退火温度和加热速度对PIF340 钢组织和再结晶织构的影响,指出PIF340钢罩式炉退火时,退火温度应按罩式炉上限控制,并保证足够的保温时间。按实验工艺进行了工业生产,产品冲压性能优良,。关键词:IF钢;再结晶;组织;织构;退火温度中图分类号:; 文献标识码:A 文章编号:1003~9996(2009)06—0009—04 Research of Batch Annealing Process forCold Rolled Adding P High Strength IFSteel Plate ZUO unl,CHANG Junl,ZHANG Kai—hual,YANG Jin— ( Iron and Steel Research Institute,Panzhihua New Steel&Vanadium Co.。Ltd.,Panzhihua ) Abstract:The recrystallization temperature ofPIF340 steel was obtained influence of nealing temperature and heating speed on microstructure and texture steelwere pointed Out that theannealing temperature should becontrolled upper-limited value batch the enough holding time should beassured industry last,the good deep-damping property product was Key words:IF steel;recrystallization;microstructure;texture;annealing temperature 1 前言随着我国汽车工业的快速发展和节约能源减轻汽车自重的需要,在汽车制造中大量采用了加磷高强IF钢冷轧板。通常情况下,深冲钢板随强度提高而成形性能下降,这给后续加工造成困难。加磷高强IF钢利用超低碳无间隙原子钢具有超深冲性的特点,与P、Mn、Si等元素的固溶强化机制相结合,超深冲性和强度均良好。研究表明,要获得综合性能优良的加磷高强IF钢,需要从微合金化、超低碳、钢质纯净及热轧、冷轧和退火工艺等方面控制¨],以获得强的再结晶织构及较粗大的铁素体晶粒。冷轧退火工艺是生产加磷高强 IF钢超
加磷高强IF钢冷轧板罩式退火工艺研究 来自淘豆网www.taodocs.com转载请标明出处.