化学镀用光亮剂研究.doc

2012届本科毕业论文(设计)
论文题目:化学镀用光亮剂研究
学生姓名:
所在院系:机电学院
所学专业:机械设计制造及自动化
导师姓名:
完成时间:2012年5 月10日
摘要
本试验是通过向镀液中加入所选用的光亮剂中间体,使用碳钢试片作为基材,以提高试片表面光亮度为目的的化学镀试验。由于光亮组分较多,所以分别进行了四因素三水平试验和三因素两水平正交试验,对各中间体浓度进行增减优化,从而找到最优配方。该配方为:DEP45mg/l, PME15mg/l, OP-10 10mg/l,VS25mg/l, BSI750 mg/l, PS200mg/l, PPS-OH400mg/l。得出最优配方后,为确保试验结果的准确性。又进行了检验试验,结果表明,该优化配方是好的。
关键词:光亮剂,正交试验,表面光亮度,化学镀。
Chemical nickel plating brightener optimization experiment
Abstract
The test principle is to add sulfuric acid nickel plating selected brightener intermediates, use carbon steel test pieces as base material, and try to improve on the surface of brightness for the purpose, chemical plating test. Will the mother material processing put in 85 ℃ after plating baths to heat preservation 40 minutes, after drying treatment using brightness measuring instrument measuring its brightness values. The orthogonal design software data analysis to determine the development plan, the four factors are three level test three factors and two levels orthogonal test, the intermediate increase or decrease concentration optimization, and find the best formula. The optimal formula that see table 1. DEP45mg/l, PME15mg/l, OP-10 10mg/l,VS25mg/l, BSI750 mg/l, PS200mg/l, PPS-OH400mg/l. The optimal formula obtained to ensure the accuracy of the test results. The inspection and test, namely the selective repeat some test.

Keywords: brightener, orthogonal test, the surface brightness, chemical plating.
目录
1 绪论 1
2 试验材料和方法 2
2
试验方案的确定 3
4
4
试验过程 6
正交试验 6
第一轮试验 6
第二轮实验 7
第三轮实验 7
第四轮实验 8
第五轮实验 8
第六轮实验 9
第七轮实验 9
第八轮实验 10
第九轮实验 10
正交试验的检验 11
检验一 11
检验二 11
检验三 12
3 试验结果与分析 13
4 结论 14
致谢 14
参考文献 14
1 绪论
光亮剂发展至今已有几十年的历史,是作为化学镀、电镀的添加剂。它可使镀层均匀,提高镀件装饰性。在保护性能方面,它能提高产品的耐蚀性,并且提高使用寿命。在功能性方面,能提高加工工件的耐磨性、润滑性能等特殊功能。
光亮剂根据作用的不同分为光亮剂,宏观分散能力改善剂也就是平滑剂,微观分散能力改善剂(整平剂),润湿剂,改性