喷墨打印用陶瓷墨水的研究现状.doc

喷墨打印用陶瓷墨水的研究现状
莫云杰,杨天睿,郑乃章
(景德镇陶瓷学院,国家日用及建筑陶瓷工程技术研究中心,景德镇 333001)
摘要:陶瓷喷墨打印技术在我国陶瓷行业受到高度关注。和传统的陶瓷印刷技术相比,陶瓷喷墨打印技术对颜料的粒径分布、平均粒径、形貌和分散性以及油墨的制备等提出了更高的要求,国内的陶瓷墨水的进口量仍较大。本文综述了陶瓷墨水的多种制备方法,并介绍了喷墨打印相比传统印刷的优势,并对喷墨打印用陶瓷墨水制备技术进行了展望。关键词:陶瓷墨水;制备方法;传统印刷
中图分类号:+3/+ 文献标识码:A 文章编号:1001-9642(2016)02-0001-04DOI:.1001-
Research Status of the Ceramic Ink for Ink-jet Printing
MO Yunjie,YANG Tianrui,ZHENG Naizhang
(Jingdezhen Ceramic Institute, National Engineering Research Center for
Domestic and Building Ceramics, Jingdezhen 333001,China)
Abstract:Ink-jet print has high level concern in ceramic industry in our country. Compared with the traditional
ceramic printing technology, the ink-jet printing has high requirements in particle size distribution, mean size, morphology, dispersion and the synthesis
of the ceramic ink. The domestic ceramic ink relies on import at present. In this article, various preparation methods of ceramic ink and the advantages of ink-jet printing relative to traditional printing are summarized. The use of ink-jet printing technology in the future is also discussed.
Key words:Ceramic ink;Preparation methods;Traditional printing
0 引言
陶瓷喷墨打印技术是借鉴了现有桌面办公系统,通过陶瓷喷墨打印机将陶瓷墨水打印到承印物上形成图案,这其中的陶瓷墨水的制备是陶瓷喷墨打印中最重要的一环,主要是通过将陶瓷色料分散在溶剂中得到。陶瓷喷墨打印可满足线条精准、简繁无忧、频繁变化和重组快捷等多样化的特殊设计思想。陶瓷墨水所要求的颗粒的直径必须要小于喷头直径的百分之一。喷头一般为
[1]
并将其与丝网印刷、滚筒印刷进行对比,以供同行今后研究和发展参考。
1 陶瓷墨水的制备方法
分散法
分散法是将所拥有的色料先通过球磨的方法球磨到喷墨打印所需求的颗粒粒径,再将球磨好的色料通过加入分散剂的形式均匀分散于墨水溶剂中来获得稳定不沉降的陶瓷墨水。
Kimura等申请了粘度为50 mPa?s色料粒径为859
nm的墨水专利[8],将所制备出来的墨水应用在陶瓷喷墨
21μm,这也就说所需要颗粒应为200 nm左右。而制备陶瓷墨水的方法有:分散法[2-3]、溶胶凝胶法[4]以及反相微乳液法[5]。本文综述了陶瓷墨水的制备方法及其特点,
收稿日期:2015-03-18基金项目:景德镇市科技局项目(701316-008)作者简介:莫云杰(1981-),女,工程师,天津人,硕士。Email:iammoyunjie@
中国陶瓷│CHINA CERAMICS│2016(52)第 2 期│1
中国陶瓷2016年第 2 期
打印机上,墨水在使用过程中不会阻塞喷嘴。
Kosmala [9],再加入N2H4OH,以F127为分散剂将得到的纳米级颗粒溶于水中再用高强度聚焦超声进行分散。
分散时间从10~90 min。之后对其分散性进行检测。如图1a是超声处理前的颗粒,可以看到颗粒之间团