连铸连轧应用.doc

连铸连轧应用薄板坯连铸连轧的发展现状及应用探讨时义祥,何绪友,王爱霞,高艳萍( 济南钢铁集团总公司,山东济南 250101) 摘要:根据薄板坯连铸连轧技术的发展现状及该工艺的关键技术, 对其产品的种类和质量做了相应的分析, 指出济钢在薄板坯连铸连轧工艺的规划建设中, 应重视工艺流程的选择、工序间的衔接及技术装备的引进等问题,以保证达产达标。关键词:薄板坯连铸连轧;近终型连铸; CSP 工艺;液芯铸轧中图分类号: TF777 文献标识码: B 文章编号: 1004-4620(2003)02-0001-03 Discussion on Current Status and Application of Thin Slab Continuous Casting and Rolling SHI Yi-xiang, HE Xu-you, WANG Ai-xia, GAO Yan-ping (Jinan Iron and Steel Group,Jinan 250101,China) Abstract : According to the current status of thin slab continuous casting and rolling and its key technologies,analyzes the kinds and quality of its products and points out that Jigang should attach importance to the choice of process flow,inter-process join and the import of technologic equipment etc. to ensure the output and targets. Key words : thin slab continuous casting and rolling; shape continuous pact strip production process;liquid casting-pressing-rolling 薄板坯连铸连轧是生产热轧板卷的新一代工艺流程, 与传统工艺流程相比, 在节约投资、缩短生产周期、提高成材率、降低生产成本等方面有明显优势。预计到 2010 年全球可建成 75 个薄板坯连铸连轧工厂,总生产能力可达到 亿t。薄板坯连铸连轧技术最初是为电炉短流程小钢厂生产板带而开发的。鉴于它在技术和经济效益方面显示出的巨大优势,逐渐受到了许多大型钢铁联合企业的重视, 目前已成功地嫁接到传统的高炉—转炉长流程钢铁生产工艺中。 1 主要生产工艺典型的薄板坯连铸连轧工艺流程由炼钢( 电炉或转炉)—炉外精炼—薄板坯连铸—连铸坯加热—热连轧等五个单元工序组成。该工艺将过去的炼钢厂和热轧厂有机地压缩、组合到一起, 缩短了生产周期, 降低了能量消耗,从而大幅度提高经济效益。 技术实质应用先进的近终型连铸技术, 将铸出的板坯厚度减薄到一临界区间, 省去传统的热轧板带机组中的粗轧机架, 在连铸机和连轧机之间给予较小的热量补充, 直接通过精轧机组轧成热轧带卷。使从钢液进入结晶器到热轧卷取完毕的时间缩短到 15~ 30min 。 工艺类型薄板坯连铸连轧技术因