TiO-CFA复合材料制备及光催化性能研究.docx

TiO/CFA复合材料制备及光催化性能研究
 
   
 
 
 
 
 
 
 
     
 
 
 
 
 
周向欣 任雪盈 张军 叶延勇
摘 要：以电厂废弃物粉煤灰作载体，钛酸丁酯为钛源，采用溶胶-凝胶法正交实验制备二氧化钛/粉煤灰（TiO2/CFA）复合材料，以亚甲基蓝为目标污染物，进行光催化处理，探究其最佳制备条件和影响因素。结果表明，TiO2/CFA最佳制备条件为负载率40%、焙烧温度500℃、，%。通过极差分析可得，影响降解性能顺序为焙烧温度>焙烧时间>负载率。TiO2/CFA能够有效的去除废水中的亚甲基蓝，具有一定的实用价值。
关键词：二氧化钛；粉煤灰；光催化；亚甲基蓝
X52 ：A ：2095-2945（2018）14-0032-03
Abstract： Titanium dioxide/coal fly ash（TiO2/CFA） composite was prepared by Sol-Gel Method using coal fly ash as carrier and butyl titanate as titanium source. Methylene blue was used as the target pollutant for photocatalytic treatment. The optimum preparation conditions and influencing factors were investigated. The results show that the optimum preparation conditions of TiO2/CFA are as follows： loading rate 40%， calcination temperature 500℃， calcination time ， and the degradation rate can reach %. Through the range analysis， the order of influencing degradation performance is calcination temperature>calcination time>loading rate. TiO2/CFA can effectively remove methylene blue from wastewater， and has certain practical value.
Keywords： titanium dioxide （TiO2）； coal fly ash （CFA）； photocatalysis； methylene blue
TiO2等半導体光催化剂负载和掺杂是提高光催化剂性能的有效途径[1]。粉煤灰是燃煤电厂排放的固体废物，近年来采用粉煤灰负载TiO2降解水中有机物研究成为热点。Xuan等研究表明粉煤灰经过处理后可作为SCR催化剂载体[2]。段瑞斌等研究了粉煤灰负载TiO2的制备方法
[3]，霍炜江等研究了硝酸化粉煤灰负载TiO2的制备及光催化性能[4-5]。然而目前研究多在于TiO2负载量对其