涂层结构与摩擦学性能研究-材料加工专业毕业论文.docx

indicates that the gradient coating has a better tribological properties than uniform coating in seawater.
Key Words: coating;Arc ion plating;Structure;Mechanical properities; Tribological properties
目 录
摘 要................................................................. I
Abstract ................................................................ II
第一章绪论............................................................. 1
课题研究背景..................................................... 1
表面改性技术及防护方法............................................ 2
真空镀膜技术................................................ 2
真空镀膜技术分类............................................ 2
化学气相沉积(Chemical Vapor Deposition, CVD) 2
物理气相沉积(PVD) 3
真空蒸发镀................................................ 4
真空溅射镀................................................ 4
真空离子镀................................................ 5
316 L 不锈钢 7
CrN 及 涂层 7
CrN 涂层 7
涂层 8
选题依据及研究内容................................................ 9
选题依据.................................................... 9
研究内容................................................... 10
第二章实验方案及研究方法............................................... 11
实验方案........................................................ 11
式样及靶材材料............................................. 11
涂层制备 11
CrN 及 涂层制备 12
均质及梯度 涂层制备 12
涂层的表征...................................................... 13
扫描电子显微镜(SEM) 13
X 射线衍射仪(XRD) 13
多功能 X 射线光电子能谱(XPS) 14
透射电子显微镜(TEM) 14
硬度、模量及结合力表征..................................... 14
耐腐蚀性表征............................................... 15
摩擦磨损表征............................................... 15
第三章 316 L 不锈钢表面沉积 涂层的结构及性能研究 17
微观结构......................................................... 17
力学性能........................................................ 19
耐腐蚀性能................................